Quality of Microstructure of Duplex Stainless Steels
Duplex stainless steels typically have 50% of both austenite and ferrite in their microstructure. It is necessary to have good
![](https://www.rolledalloys.com/wp-content/uploads/flat-bar-rolled-alloys-1.jpg)
Flat Bar or Gauered Flat Bar from Plate
Discover the difference between flat bars and gauered flat bars cut from plates. Learn about their dimensional tolerances and the
![](https://www.rolledalloys.com/wp-content/uploads/ra330-metal-dusting-corrosion-Rolled-Alloys.jpg)
Metal Dusting
Metal Dusting is a hazard when using heat-treat carburizing furnaces and petrochemical equipment. Explore how high-chromium alloys thwart this destructive
![](https://www.rolledalloys.com/wp-content/uploads/stainless-steel-process-rolled-alloys.jpg)
Manganese Substitution Grades of Stainless Steel
Explore the evolution of stainless steel with manganese substitution grades, offering cost-effective solutions for industries like appliances and food equipment.
Alloy X
Alloy X is one of the most widely used nickel base superalloys for gas turbine engine components. This solid solution strengthened grade has good strength and excellent oxidation resistance to 2000°F. Alloy X has excellent resistance to reducing and carburizing atmospheres, making it suitable for furnace components. Due to its high molybdenum content, Alloy X may be subject to catastrophic oxidation at 2200°F.
Alloy X is welded by all common methods such as gas tungsten arc, gas metal arc, shielded metal arc, electron beam and resistance welding. Use matching filler metal, keep interpass temperature low. After severe forming, fabrications may be annealed 2150°F, 15 minutes per 1/8″ of thickness, rapid air cool.
- Good high temperature strength
- Oxidation resistance through 2000°F
- Carburization resistant
UNS: N06002
W. NR.: 2.4665
ASTM: B 435, B 572
ASME: SB 435, SB 572, SECT. IX P NO. 43, SECTION IX P NO. 43, SFA 5.14
AMS: 5536, 5754, 5798
GE: B50A436, B50T83, B50TF24
PDS: 1038 (X-LOW), 15102QFC
- Combustion liners
- Turbine exhaust components
- Aircraft cabin heaters
- Transition Ducts